压力校验仪的压力单位换算表
 
单位
 Pa
 KPa
 MPa
 bar
 mbar
 kgf/cm2
 cmH2O
 mmH2O
 mmHg
 p.s.i
 
Pa
 1
 10-3
 10-6
 10-5
 10-2
 10.2×
10-6
 1.02×10-3
 101.97×
10-3
 7.5×
10-3
 0.15×10-3
 
KPa
 103
 1
 10-3
 10-2
 10
 10.2×
10-3
 10.2
 101.97
 7.5
 0.15
 
MPa
 06
 103
 1
 10
 104
 10.2
 1.02×103
 101.97×103
 7.5×103
 0.15×103
 
bar
 105
 102
 10-1
 1
 103
 1.02
 1.02×103
 10.2×103
 750.06
 14.5
 
mbar
 102
 10-1
 10-4
 10
 1
 1.02×
10-3
 1.02
 10.2
 0.75
 14.5×10-3
 
kgf/cm2
 98066.5
 98.07
 98.07×
10-3
 0.98
 980.67
 1
 1000
 10.000
 735.56
 14.22
 
cmH2O
 98.06
 98.07×
10-3
 98.07×
10-6
 0.98×
10-3
 0.98
 10-3
 1
 10
 0.74
 14.22×103
 
mmH2O
 9.806
 9.807×
10-3
 9.807×
10-6
 98.07×
10-6
 98.07×
10-3
 10-4
 0.1
 1
 73.56×
10-3
 1.42×10-3
 
mmHg
 133.32
 133.32×
10-3
 133.32×
10-6
 1.33×
10-3
 1.33
 1.36×
10-3
 1.36
 13.6
 1
 19.34×10-3
 
p.s.i
 6894.76
 6.89
 6.89×
10-3
 68.95×
10-3
 68.95
 70.31×
10-3
 70.31
 703.07
 51.71
 1
 

关于隔离膜片部分耐蚀材料的选择
 
腐蚀介质
 耐腐蚀材料
 
锡青铜(QSn6.5-0.4)
 SUS316
 纯钽(Ta)
 蒙耐尔(Ni70Cu30)
 哈氏合(HC)
 聚四氟乙烯（F4）
 
硫酸（H2SO4）
 V
 △
 ○
 V
 V
 V
 
硝酸（HNO3）
 ╳
 V
 ○
 ╳
 V
 V
 
盐酸（HCI）
 △
 ╳
 ○
 ╳
 V
 V
 
磷酸（H3PO4）
 V
 V
 ○
 V
 V
 V
 
醋酸（CH3COOH）
 V
 V
 ○
 V
 ○
 V
 
烧碱（NaOH）
 △
 ○
 △
 ○
 ○
 V
 
纯碱（Na2CO3）
 ○
 ○
 ○
 ○
 V
 V
 
小苏打（NaHCO3）
 V
 ○
 ○
 ○
 ○
 V
 
氯气（CI）
 干：V
湿：╳
 干：V
湿：╳
 ○
 干：V
湿：╳
 V
 V
 
溴（Br2）
 干：△
湿：╳
 干：╳
湿：△
 ○
 干：○
湿：╳
 ○
 V
 
氨水（NH3）
 ╳
 V
 ╳
 ╳
 ○
 V
 
海水（30％ NaCI）
 V
 V
 ○
 ○
 ○
 V
 
符号说明：○——最佳；△——有条件使用；V——可以使用；╳——不可以使用。
 

本公司一般的选用材料为SUS316-0Cr17Ni12m，以上耐蚀材料选择为常温情况，对在特殊情况下耐蚀材料的选择请与我公司具体垂询。